Carbon-fiber composites
Carbon-fiber composites
A carbon-fiber composite direction based on Thermoplastic resin. Consider fiber distribution, structural design and processing to assess lightweight and stiffness requirements together.
SELECTION / APPLICATION
Define the matrix, carbon-fiber content and fiber length before evaluating structure and processing.
PROPERTY REFERENCE
Public catalog reference · not a grade-specific TDS
These figures support material selection. Check reference values against the grade, test standard and specimen condition; unconfirmed items require formal documentation and are not acceptance criteria.
Source checked: 2026.10.24 · Public reference figures available
| Property | Corporate reference | Conditions & documentation |
|---|---|---|
| Tensile strength | 200 - 300 MPa | Test method, specimen state and conditioning not stated |
| Tensile modulus | 15,000–35,000 MPa | Test method, specimen state and conditioning not stated |
| Elongation at break | 1-3% | Test method, specimen state and conditioning not stated |
| Flexural modulus | 15,000–30,000 MPa | Test method, specimen state and conditioning not stated |
| Property | Corporate reference | Conditions & documentation |
|---|---|---|
| Melting point (PA66) | 255 - 265 °C | Method not stated; confirm service temperature against load and lifetime |
| Melting point (PA6) | 220 - 225 °C | Method not stated; confirm service temperature against load and lifetime |
| HDT (0.45 MPa) | 200–250°C | Load as stated in the property name; other method and conditioning details not stated |
| HDT (1.82 MPa) | 180–230°C | Load as stated in the property name; other method and conditioning details not stated |
| Continuous use temperature | 100–150°C | Method not stated; confirm service temperature against load and lifetime |
| Flammability (UL 94) | HB (V-0 grades available) | Specimen thickness and grade not stated; not a certification claim |
PROCESSING / VALIDATION
Corporate processing figures are a starting point for trials. Confirm actual settings against the grade, moisture content, equipment, mold and wall thickness.
| Property | Corporate reference | Conditions & documentation |
|---|---|---|
| Drying temperature | 80 - 100°C | Website processing reference; verify with the grade, equipment and part trials |
| Drying time | 4 - 8hrs | Website processing reference; verify with the grade, equipment and part trials |
| Melt temperature (PA66) | 280 - 310 °C | Website processing reference; verify with the grade, equipment and part trials |
| Mold temperature | 80 - 100 °C | Website processing reference; verify with the grade, equipment and part trials |
| Injection pressure | 80–140 MPa | Website processing reference; verify with the grade, equipment and part trials |
Stiffness & mass: evaluate weight reduction with matching geometry and load
Anisotropy: verify flow-direction and transverse properties separately
Processing & dimensions: check fiber condition, warpage and assembly
APPLICATION CONNECTIONS
Discuss the specific application through the target part, environment and performance needs.
GRADE / DOCUMENTS
Request the grade, revision date, test standards, conditioning and property range.
Request documents →Confirm safety documentation for the material and supply region.
Request documents →Confirm batch records, identification and the inspection scope for the project.
Request documents →EXPLORE RELATED MATERIALS
Transparent nylon 12↗A transparent nylon 12 for selection around optical clarity, resilience and toughness in transparent structures, electronics and industrial products.
Transparent nylon 12↗An amorphous transparent nylon combining stiffness, low water uptake and chemical resistance for automotive, electronic and packaging applications.
Transparent nylon 12↗A high-transmission transparent nylon 12 for evaluating toughness and stress-cracking resistance in optical parts, clear housings and industrial components.
MATERIALS / ENGINEERING / POSSIBILITIES